Erection requirements for API standard 650 low-alloy steel tanks
API 650 is an American standard for welding flat bottom vertical storage tanks. This API standard 650 low-alloy steel tanks standard specifies requirements for the design, manufacturing, welding, inspection and installation of storage tanks. API 650 is widely used in storage tanks designed to withstand low internal pressures and used to store typical products such as API standard 650 low-alloy steel tanks crude oil, gasoline, chemicals and water. BBN has extensive experience in API 650 tanks, from +/- 500 cubic meters of tanks produced in the factory to +/- 15000 cubic meters of tanks produced on site.
API standard 650 low-alloy steel tanks Visual InspectionUpon completion of all the foregoing tests, the pressure in the tank shall be released and a thorough visual inspection shall be made of both the inside and outside of the tank, giving particular attention to all internal ties, braces, trusses, and their attachments to the walls of the tank. Anchors shall be checked for snug tightness and adjusted if required. Anchor threads shall be fouled by peening or tack welding to prevent loosening. In lieu of thread fouling, double nuts may be used.Rate of Water Filling and Water TemperatureThe rate at which water is introduced into a tank for a hydrostatic test shall not exceed 3 ft of depth per hour. The foundation, venting equipment, or other conditions may limit the water filling to a lower rate. Pressure shall not be applied above the surface of the water before the tank and its contents are at about the same temperature.
Some defects may be found after the regular safety inspection for the API standard 650 low-alloy steel tanks. The common API standard 650 low-alloy steel tanks defects are: Tank cracks, tank welding defects. The cracks on the base metal, surface and near surface of the tank wall shall be eliminated by grinding with circular arc, and then magnetic particle inspection or re inspection shall be carried out. Cracks in heat affected zone: generally, grinding method is used to eliminate cracks, and magnetic particle or dye flaw detection is used to confirm that there is no crack, and then repair welding or grinding smooth transition.
We have a high-quality elite team, with a wealth of steel products resources and business experience. The company has established a perfect career development channel to provide all employees with broad job development opportunities, clear career planning, so that the potential can be fully explored, talent can be fully exploited, and a platform for employees to realize the value of life can be built, so as to realize the common growth and development with employees in the long-term development of the company.
The predecessor of Ningbo port is Ningbo Port Authority. Ningbo port consists of Beilun port, Zhenhai port, Ningbo port, Daxie port and Chuanshan port. It is a multi-functional and comprehensive modern deep-water port integrating inland river port, estuary port and seaport.
We should focus on the main problems to be solved and pay attention to efficiency. After receiving the user's quality objection report data, the possible causes, responsible units, compensation amount, etc. of the problem shall be judged based on experience. To have a clear service plan, to be clear about what your main problem is, what technical support is needed, these should be prepared.