API standard 650 low-alloy steel tanks design metal temperature

We can process the steel materials according to your drawing. Or if you can not make drawing, please send us API standard 650 low-alloy steel tanks specific data and requirements, our technical department can make design and drawing for you, and then confirm with your technician or engineer. If all is OK, our processing center will process the steel materials according to the drawing. So no matter what size and shapes you need, we can meet demands at the most time.

Prefabrication requirements for API standard 650 low-alloy steel tanks, large vertical storage tanks:
1. The machined surface of the edge of the steel plate should be smooth, and there should be no defects such as slag inclusion, delamination, cracks, etc., and the surface hardened layer produced by the flame cutting groove should be removed.
2. Dimension deviation after steel plate processing: the deviation of plate width is less than 1.5 mm, the deviation of plate length is less than 2 mm, and the difference between diagonals is less than 3 mm.

Thickness as it Affects Preheat and Post-heat Requirements
Plate with thicknesses below 1/2 in. is reasonably notch tough. In most steels, when the API standard 650 low-alloy steel tanks used plate thickness exceeds 3/4 in. – 1 in., notch toughness, particularly as welded, decreases sharply. The decrease in notch toughness can be minimized by the conventional post-heat treatment and, in many steels, by preheat treatment. The benefits of preheat treatment in steels 3/4 in. – 1 in. thick have been demonstrated; similar benefits could be expected in thicker steels, but sufficient experimental data are currently lacking.