API 650 petroleum storage tank pipeline stress and product pressure, tank pressure, uniform or non-uniform temperature difference between the tank wall and the tank bottom, which cause the radial displacement and longitudinal rotation of the API standard 650 aluminum tanks tank wall at the opening to affect the oil tank wall The impact is obvious. Therefore, the design must ensure that the load applied by the external pipeline on the opening of the tank wall is within the safety limit. If the stress of the API standard 650 aluminum tanks connecting piping is not handled properly, the wall of the API 650 petroleum storage tank may deform or even rupture, causing a major accident.

Surface Inspection of low-pressure storage tank Component PartsBefore assembly, unless already so certified by shop inspectors, all sidewall plates or sections and roof and bottom plates shall be inspected for thickness, freedom from injurious defects, and soundness of any welded joints.Check of Dimensions of API standard 650 aluminum tanks Component PartsAll formed plates and curved sections shall be checked for conformance with the planned dimensions and cross section. For unusual repairs the inspector should keep a record of measurements taken at sufficient intervals to constitute a satisfactory record.Check of Chemical and Physical Property DataThe inspector shall check the material being assembled by the lists of the plates from the mill, their heat numbers, chemical analyses, and mechanical properties as given on mill reports and shall see that copies are available to be attached to the Manufacturer’s report.

Treatment of API standard 650 aluminum tanks welding defects:
1. Lack of fusion: once found, it should be shoveled and grinded off before re welding.
2. Incomplete penetration: over standard defects shall be removed and re welded. When welding on both sides, the shallow side of the groove can be grinded and shoveled to expose the welding root on one side, and then the welding is repaired.
3. Slag inclusion: over standard defects shall be removed and re welded.
4. Crater: weld to full after grinding.
5. Air hole: if the internal air hole exceeds the standard, it shall be welded again after being removed by grinding shovel, and the surface air hole shall be removed by grinding wheel and then repaired.

The company revolves around the long-term strategy of "building a quality base and building a century-long BEBON", adheres to the development ideas of innovation, transformation, and improvement, vigorously promotes transformation and upgrading, structural adjustment, energy conservation and emission reduction, and strives to create high-quality steel with strong core competitiveness and distinctive features The production base has become a green steel city with intensive land use, clean production, efficient use of resources, harmonious and friendly production and environment, business and society, and BEBON characteristics.

Using advanced logistics management, advanced models and management experience to increase the reliability of logistics operations and provide customers with 24/7 cargo management. On the premise of reducing transportation and management costs as much as possible, we provide customers with high-quality and efficient services; good business reputation has been recognized and supported by our customers.

We should focus on the main problems to be solved and pay attention to efficiency. After receiving the user's quality objection report data, the possible causes, responsible units, compensation amount, etc. of the problem shall be judged based on experience. To have a clear service plan, to be clear about what your main problem is, what technical support is needed, these should be prepared.